1. 商品介绍
  2. 藕联剂表面处理石英粉,云母粉,氢氧化铝,阻燃剂
氢氧化铝阻燃剂TRIKUP-A300-GG1

氢氧化铝阻燃剂TRIKUP-A300-GG1

TRIKUP是ATH以Amino silane表面改性, 用作阻燃功能填料。
TRIKUP - 一般ATH填充化合物最受欢迎的等级, 需要在弯曲和抗拉强度方面得到更多的提升, 及提高耐湿性和耐热性, 并且改善高聚合物母料的分散性, 如环氧树脂、聚酯纤维、PBT塑料、酚醛、三聚氰胺和丙烯酸树脂。
TRIKUP is ATH surface modified with Amino silane coupling agent, use as flame-retardant filler. 
TRIKUP - the most popular grade for general ATH filled compound which needs more
Improvement in the flexural and tensile strength , and increases moisture and heat resistance as well as improves dispersion in the high polymer martrix , such as Epoxy , Polyester , PBT , Phenolic , Melamine and Acrylic Resins .
The typical properties and data as following :  Al(OH)3  98
L.O.I.                      34.00 (Total on 110o ~ 1100oC)

Moisture                       0.5 (at 110oC)

Bulk Density ( g/cm3)     0.70 ~ 1.30

Specific Gravity                     2.42

Moh’s Hardness               2.50 ~ 3.50

Refractive Index                   1.57

Brightness                         > 90

Particle Size , Wt% on 200 mesh  / Min. 98 (Through 325 mesh)

Median Particle Size (µm)             9.0 ~ 14.00

矽石塑固粉-石英粉表面处理NOVACOP-207 / 625 GA-1

NOVACOP 207/625-GA-1 为制造工业涂料和用於对水气/化学耐受性极端要求涂层的最适宜的等级。(以氨基矽烷藕联剂表面处理)。
NOVACOP 207/625-GA-1 are the most suitable and popular grades in formulate industrial paints & coatings for extreme critical inquiring to water/chemical resistance. (With Amino silane coupling surface treated). 
NOVACOP 的两种重要改性趋向:
改善分散性和利用附著在表面的藕合功能,以交联成聚合物,如环氧树脂、聚酯、PBT、苯酚和丙烯酸树脂等。
NOVACOP tends to make two important changes:
Improved dispersion and the utilization of the functional coupling attached to the surface to cross-link into polymers such as Epoxy , Polyester , PBT , Phenolic & Acrylic Resins ect.
NOVACOP 可应要求提供任何类型藕联剂的表面处理作业。
NOVACOP can be processed to offer surface pendant groups with any kinds of coupling agent upon request.
***
应用於抗刮及高硬度涂料,适用於Acrylic 机壳烤漆用之
微米涂料补强填充材,
市场上销售供应长达40年以上。
特性: 
1. NOVACOP 207 GA-1
( Average Particle Size   3.5 ~ 4.9 µm)
2. NOVACOP 625 GA-1
( Average Particle Size 10.0 ~ 15  µm)

SiO2 ≥ 99%
Oil Adsorption   17 ~ 20 %


特徵Features

片状或板状                                                                       Lamellar or Platy Shape

可湿的                                                                                       Wettable                                                       

无气孔                                                                                       No porosity

最低吸油率                                                                        17Lowest oil absorption 17%

折射率通常低於树脂体系        Refractive index is typically lower than the resin system

高介电和绝缘性能–“石英”  High dielectric and insulating properties – “it’s quartz”

化学惰性                                                                               Chemically inert

防腐蚀性能                         Anti-corrosive qualities

接近纯石英                                                                  (  99.49%

无水分                               Zero moisture

莫氏硬度7                          Mohs hardness  7

 
附注:
详细规格资料欢迎来电洽询...
不可使用高压力(高剪力)分散机。
(因本材料莫氏硬度为 7会产生机台磨耗情况)

矽灰石~塑固粉WK-405G

敝公司进口针状微粉矽灰石粉,以美国专利矽烷耦连剂处理之优良产品,应用於一般高性能天然与合成胶料及氟化橡胶中,有提高定伸强度、耐酸硷性、低压缩性,并可用於各种工程塑胶中作为优良补强材料,有极佳尺寸稳定性、改进耐冲击性、提升定伸强度等物理特性,可有效(部份)取代玻纤以及改善作业性等优点,为浅色补强剂
熔点(Melting Point) : 1540。C
莫氏硬度(Moh's Hardness) : 4.5
细度(Fineness) : >97.5% Pass 325 mesh
主成份:天然CaSiO3 (Wallastonite);
平均长径比:(L/D Ratio)10~15;
         色泽:GE Brightness 90度。

云母塑固粉COPLAST MICA / LUMINA 929A

矽耦合剂表面处理分散性良好 ,  耐水性 , 耐油性 , 耐化学性 , 耐冲击性 , 耐屈曲劣化性还具有良好的绝缘和耐热性等特殊性,为塑胶、涂料之优良补强用材料;同时LUMINA 929A 云母塑固粉独特之莹光特质为制作优良商品附加价值之极品云母粉