氫氧化鋁阻燃劑TRIKUP-A300-GG1

氫氧化鋁阻燃劑TRIKUP-A300-GG1

TRIKUP是ATH以Amino silane表面改性, 用作阻燃功能填料。
TRIKUP - 一般ATH填充化合物最受歡迎的等級, 需要在彎曲和抗拉強度方面得到更多的提升, 及提高耐濕性和耐熱性, 並且改善高聚合物母料的分散性, 如環氧樹脂、聚酯纖維、PBT塑料、酚醛、三聚氰胺和丙烯酸樹脂。
TRIKUP is ATH surface modified with Amino silane coupling agent, use as flame-retardant filler. 
TRIKUP - the most popular grade for general ATH filled compound which needs more
Improvement in the flexural and tensile strength , and increases moisture and heat resistance as well as improves dispersion in the high polymer martrix , such as Epoxy , Polyester , PBT , Phenolic , Melamine and Acrylic Resins .
The typical properties and data as following :  Al(OH)3  98
L.O.I.                      34.00 (Total on 110o ~ 1100oC)

Moisture                       0.5 (at 110oC)

Bulk Density ( g/cm3)     0.70 ~ 1.30

Specific Gravity                     2.42

Moh’s Hardness               2.50 ~ 3.50

Refractive Index                   1.57

Brightness                         > 90

Particle Size , Wt% on 200 mesh  / Min. 98 (Through 325 mesh)

Median Particle Size (µm)             9.0 ~ 14.00

矽石塑固粉-石英粉表面處理NOVACOP-207 / 625 GA-1

NOVACOP 207/625-GA-1 為製造工業塗料和用於對水氣/化學耐受性極端要求塗層的最適宜的等級。(以氨基矽烷藕聯劑表面處理)。
NOVACOP 207/625-GA-1 are the most suitable and popular grades in formulate industrial paints & coatings for extreme critical inquiring to water/chemical resistance. (With Amino silane coupling surface treated). 
NOVACOP 的兩種重要改性趨向:
改善分散性和利用附著在表面的藕合功能,以交聯成聚合物,如環氧樹脂、聚酯、PBT、苯酚和丙烯酸樹脂等。
NOVACOP tends to make two important changes:
Improved dispersion and the utilization of the functional coupling attached to the surface to cross-link into polymers such as Epoxy , Polyester , PBT , Phenolic & Acrylic Resins ect.
NOVACOP 可應要求提供任何類型藕聯劑的表面處理作業。
NOVACOP can be processed to offer surface pendant groups with any kinds of coupling agent upon request.
***
應用於抗刮及高硬度塗料,適用於Acrylic 機殼烤漆用之
微米塗料補強填充材,
市場上銷售供應長達40年以上。
特性: 
1. NOVACOP 207 GA-1
( Average Particle Size   3.5 ~ 4.9 µm)
2. NOVACOP 625 GA-1
( Average Particle Size 10.0 ~ 15  µm)

SiO2 ≧ 99%
Oil Adsorption   17 ~ 20 %


特徵Features

片狀或板狀                                                                       Lamellar or Platy Shape

可濕的                                                                                       Wettable                                                       

無氣孔                                                                                       No porosity

最低吸油率                                                                        17Lowest oil absorption 17%

折射率通常低於樹脂體系        Refractive index is typically lower than the resin system

高介電和絕緣性能–“石英”  High dielectric and insulating properties – “it’s quartz”

化學惰性                                                                               Chemically inert

防腐蝕性能                         Anti-corrosive qualities

接近純石英                                                                  (  99.49%

無水分                               Zero moisture

莫氏硬度7                          Mohs hardness  7

 
附註:
詳細規格資料歡迎來電洽詢...
不可使用高壓力(高剪力)分散機。
(因本材料莫氏硬度為 7會產生機台磨耗情況)

矽灰石~塑固粉WK-405G

敝公司進口針狀微粉矽灰石粉,以美國專利矽烷耦連劑處理之優良產品,應用於一般高性能天然與合成膠料及氟化橡膠中,有提高定伸強度、耐酸鹼性、低壓縮性,並可用於各種工程塑膠中作為優良補強材料,有極佳尺寸穩定性、改進耐衝擊性、提昇定伸強度等物理特性,可有效(部份)取代玻纖以及改善作業性等優點,為淺色補強劑
熔點(Melting Point) : 1540。C
莫氏硬度(Moh's Hardness) : 4.5
細度(Fineness) : >97.5% Pass 325 mesh
主成份:天然CaSiO3 (Wallastonite);
平均長徑比:(L/D Ratio)10~15;
         色澤:GE Brightness 90度。

雲母塑固粉COPLAST MICA / LUMINA 929A

矽耦合劑表面處理分散性良好 ,  耐水性 , 耐油性 , 耐化學性 , 耐衝擊性 , 耐屈曲劣化性還具有良好的絕緣和耐熱性等特殊性,為塑膠、塗料之優良補強用材料;同時LUMINA 929A 雲母塑固粉獨特之瑩光特質為製作優良商品附加價值之極品雲母粉



特性如下
:

 

1) 325Mesh    通過           95%               4) 比重 Sp.gr.                 2.76±0.02

2) 白度 Brightness ≧   82%               5) 假比重 Bulk Density ≦   0.20g/cm3

3) 酸鹼值 pH Value    7.58.5          6) 硬度 Hardness            2.5