RM-93611粉状橡胶改性酚醛树脂(碟式煞车蹄片专用)Powder Rubber Modified phenolic resin (special for disc brake shoe)
NBR-橡胶改性树脂,淡黄棕色粉末.
NBR-Rubber Modified phenolic resin, yellowish brown powder.
NBR-Rubber Modified phenolic resin, yellowish brown powder.
| 特性 Properties : | |
| 软化点Soft point | 95~110°C |
| 胶化时间Gelation time | @150°C/sec 45~60 |
| 流动性Flow | m/m@125°C 10~35 |
| 粒度Grain Size | 200mesh pass 95%min. |
| 包装Package | 20Kg/Bag |
RM-18389粉状橡胶改性酚醛树脂(碟式煞车蹄片专用)Powder Rubber Modified phenolic resin (special for disc brake shoe)
高量NBR橡胶改性树脂,淡黄棕色粉末.
High volume NBR-Rubber modified resin, yellowish brown powder.
| 特性 Properties : | |
| 软化点Soft point | 95~100°C |
| 胶化时间Gelation time | @150°C/sec 45~60 |
| 流动性Flow | m/m@125°C 10~30 |
| 粒度Grain Size | 200mesh pass 95%min. |
| 包装Package | 15Kg/Box |
PF-6815A 摩擦材料专用无改性酚醛树脂(低游离酚)Non-modified phenolic resin for friction materials (low free phenol)
#产品中固化剂含量高,成品硬度高且耐热性好,(固化剂多寡影响成品的性能)#
High curing agent content in the product, high hardness of the finished product and good heat resistance, (the amount of curing agent affects the performance of the finished product)
淡黄色粉末.(Light yellow powder)
High curing agent content in the product, high hardness of the finished product and good heat resistance, (the amount of curing agent affects the performance of the finished product)
淡黄色粉末.(Light yellow powder)
| 特性 Properties : | |
| 游离酚Free Phenol | (0.3~0.8)% |
| 六甲基四铵Hexamine | (9.0±0.3)% |
| 胶化时间Gelation time | @150°C/sec 80~95 |
| 流动性Flow | m/m@125°C 43~51 |
| 粒度Grain Size | 200mesh pass 98%min. |
| 包装Package | 20/25Kg/Bag |
PR-2685 摩擦材料专用特殊CNSL改性酚醛树脂Special CNSL modified phenolic resin for friction materials
主要为鼓式刹车片之应用，提供优良性能与经济性,并且在质量上优於其它厂商所生产之酚醛树脂.
Mainly for the application of drum brake tablets, to provide excellent performance and economy, and better quality than other manufacturers produced phenolic resins.
#特性 specific property#
1.摩阻性能优异；2.结合强度大；3.热挠曲性适当；4.抗冲击性佳；5.加工性良好。
1. Excellent friction resistance; 2. Strong bonding strength; 3. appropriate thermal deflection; 4. Excellent impact resistance; 5. Good processability.
PR-2685除了可良好应用在一般非石棉或半金属之"鼓式煞车片"亦可应用於"离合器片"制品。
PR-2685 In addition to good application in the general non-asbestos or semi-metallic "drum brake" can also be used in "clutch chip" products.
| 特性 Properties : | |
| 软化点Soft point | 95~110°C |
| 比重Specific gravity | 1.2±0.10 |
| 粒度Grain Size | 200mesh pass 98%min. |
| 包装Package | 25Kg/Bag |
PR-685 橡胶工业用增硬及补强性酚醛树脂Hardened and reinforced phenolic resins for rubber industry
PR-685是进口特种油变性原料合成生产之特殊油变反应性酚醛树脂，广泛应用於橡胶增硬作用，除一般合成及天然橡胶之使用外，由於PR-685的特殊油变性对於极性橡胶(如NBR、CR等)，具有优良的亲和性，为极有效的反应性补强材料。
PR-685 is a special oil-reactive phenolic resin for the synthesis and production of imported special oil denatured raw materials, widely used in rubber hardening, in addition to the general synthesis and use of natural rubber, due to the special oil degeneration of PR-685 for polar rubber (such as NBR, CR, etc.), with excellent affinity, As a highly effective reactive reinforcement material.
[注: PR-685 含有7.5% hexamine，PR-685(U)为不含hexamine产品]。
[Note: PR-685 contains 7.5% hexamine,PR-685 (U) for products that do not contain hexamine].
W-885K---砂轮研磨片专用改性树脂Special modified resin for grinding wheel grinding sheet
浅黄到淡棕色粉末yellow pale to light brown powder
| 特性 Properties : | |
| 比重Specific gravity | 1.2±0.10 |
| 游离酚Free Phenol | ≤ 3% |
| 六甲基四铵Hexamine | (8.0~9.0)% |
| 胶化时间Gelation time | @150°C/sec 45~65 |
| 流动性Flow | m/m@125°C 26~36 |
| 粒度Grain Size | 200mesh pass 98%min. |
| 包装Package | 25Kg/Bag |