高性能粉狀酚醛樹脂( High functional Phenolic Resin powder )3
RM-93611粉狀橡膠改性酚醛樹脂(碟式煞車蹄片專用)Powder Rubber Modified phenolic resin (special for disc brake shoe)

RM-93611粉狀橡膠改性酚醛樹脂(碟式煞車蹄片專用)Powder Rubber Modified phenolic resin (special for disc brake shoe)

NBR-橡膠改性樹脂,淡黃棕色粉末.
NBR-Rubber Modified phenolic resin, yellowish brown powder.

特性 Properties :
軟化點Soft point 95~110°C
膠化時間Gelation time @150°C/sec 45~60
流動性Flow m/m@125°C 10~35
粒度Grain    Size  200mesh pass 95%min.
包装Package 20Kg/Bag

RM-18389粉狀橡膠改性酚醛樹脂(碟式煞車蹄片專用)Powder Rubber Modified phenolic resin (special for disc brake shoe)

高量NBR橡膠改性樹脂,淡黃棕色粉末.
High volume NBR-Rubber modified resin, yellowish brown powder.

特性 Properties :
軟化點Soft point 95~100°C
膠化時間Gelation time @150°C/sec 45~60
流動性Flow m/m@125°C 10~30
粒度Grain    Size  200mesh pass 95%min.
包装Package 15Kg/Box

 

PF-6815A 摩擦材料專用無改性酚醛樹脂(低游離酚)Non-modified phenolic resin for friction materials (low free phenol)

#產品中固化劑含量高,成品硬度高且耐熱性好,(固化劑多寡影響成品的性能)#
High curing agent content in the product, high hardness of the finished product and good heat resistance, (the amount of curing agent affects the performance of the finished product)
淡黃色粉末.(Light yellow powder)

特性 Properties :
游離酚Free Phenol (0.3~0.8)%
六甲基四銨Hexamine  (9.0±0.3)%
膠化時間Gelation time @150°C/sec 80~95
流動性Flow m/m@125°C 43~51
粒度Grain    Size  200mesh pass 98%min.
包装Package 20/25Kg/Bag

PR-2685 摩擦材料專用特殊CNSL改性酚醛樹脂Special CNSL modified phenolic resin for friction materials

主要為鼓式剎車片之應用,提供優良性能與经濟性,並且在質量上優於其它廠商所生產之酚醛樹脂.
Mainly for the application of drum brake tablets, to provide excellent performance and economy, and better quality than other manufacturers produced phenolic resins.




#特性 specific property#
1.摩阻性能優異;2.结合强度大;3.熱撓曲性適當;4.抗冲擊性佳;5.加工性良好。
1. Excellent friction resistance; 2. Strong bonding strength; 3. appropriate thermal deflection; 4. Excellent impact resistance; 5. Good processability.
PR-2685除了可良好應用在一般非石棉或半金屬之"鼓式煞車片"亦可應用於"離合器片"製品。
PR-2685 In addition to good application in the general non-asbestos or semi-metallic "drum brake" can also be used in "clutch chip" products.
特性 Properties :
軟化點Soft point 95~110°C
比重Specific gravity 1.2±0.10
粒度Grain    Size  200mesh pass 98%min.
包装Package 25Kg/Bag

PR-685 橡膠工業用增硬及補強性酚醛樹脂Hardened and reinforced phenolic resins for rubber industry





PR-685是進口特種油變性原料合成生產之特殊油變反應性酚醛樹脂,廣泛應用於橡膠增硬作用,除一般合成及天然橡膠之使用外,由於PR-685的特殊油變性對於極性橡膠(如NBR、CR等),具有優良的親和性,為極有效的反應性補強材料。
PR-685 is a special oil-reactive phenolic resin for the synthesis and production of imported special oil denatured raw materials, widely used in rubber hardening, in addition to the general synthesis and use of natural rubber, due to the special oil degeneration of PR-685 for polar rubber (such as NBR, CR, etc.), with excellent affinity, As a highly effective reactive reinforcement material.

[註: PR-685 含有7.5% hexamine,PR-685(U)為不含hexamine產品]。

[Note: PR-685 contains 7.5% hexamine,PR-685 (U) for products that do not contain hexamine].

 

W-885K---砂輪研磨片專用改性樹脂Special modified resin for grinding wheel grinding sheet

淺黃到淡棕色粉末yellow pale to light brown powder

特性 Properties :
比重Specific gravity 1.2±0.10
游離酚Free Phenol ≦ 3%
六甲基四銨Hexamine  (8.0~9.0)%
膠化時間Gelation time @150°C/sec 45~65
流動性Flow m/m@125°C 26~36
粒度Grain    Size  200mesh pass 98%min.
包装Package 25Kg/Bag